Two component room temperature curing fluid compound which cures with low shrinkage to a strong flexible mould rubber liquid LH-9040 # has good elongation, high tear strength and excellent release characterristics. Mould rubber will reproduce finite details from patterns of wood, glass. Metal, and other materials.A highly anti-adherent flexible compound that is extremely suitable for reproduction of fine details , it has high temperature and chemcal resistance making it well suited for ll types of casting resins, polyester, polyurethane and epoxy.
TECHNICAL PROPERTIES
Appearance (component A) : Clear Component B (Hardner) : clear liquid
Viscosity (cps) : 85000(at +23) 800
Mixing ratio (mould rubberA+B Harder) : 10 : 1 parts in weight
Work Time(at + 20) : 30 minutes
Demoulding time (at +20) : 8-12 hours
Specific gravity : 1.220 (at + 20))
Hardness (Shore A) At 2mm cured : 37 ± 3
Tensile Strength kg/c(MPA) : 10
Tear strength kgf / cm ( KN/M) : 14